Pre-Heating effect on the microhardness and depth of cure of Bulk-Fill composite resins / Efecto del precalentamiento de las resinas compuestas Bulk-Fill en la microdureza y la profundidad de curado

Abstract The aim of this study was to investigate the effect of preheating three bulk-fill and one conventional composite resin on the Vickers microhardness and depth of cure of these composites. In this study, three bulk-fill composites- SDR Plus (SDR), Estelite BULK FILL Flow (EST), Admira® Fusion x-tra (AFX), and one conventional composite resin G-ænial POSTERIOR (GP) were used as the control group. The samples were obtained at room temperature (24°C) and at 55°C in T2 mode after being placed in a heating device for 10 minutes. The samples were divided into eight groups (n=10) according to the type of material and heating process that was utilized (preheated and nonheated). All samples were tested with a Vickers microhardness (VHN) tester on the bottom and top surfaces. The first measurements were obtained at baseline; the second set of measurements was performed after the samples were stored in distilled water at 37°C for 24 hours. The depth of cure was calculated using a bottom/top hardness ratio of measurements. Statistical analysis was performed utilizing the SPSS V23 and Shapiro-Wilk tests. Lastly, the Duncan test was used for multiple comparisons (p<0.05). While the VHN increased after the preheating procedure in bulk-fill composites, it decreased in GP. There was no difference between the baseline and the 24-hour VHN values in SDR and GP. After 24 hours, while the VHN of EST increased, the VHN of AFX decreased. There was no difference between the hardness ratios of the AFX and EST samples (p<0.001) and hardness ratios were greater than GP and SDR. When comparing the baseline and the 24- hour values, the VHN depended on the type of materials. Sufficient curing depth was obtained in all groups with a thickness of 2mm.

Resumen El objetivo fue investigar el efecto del precalentamiento de tres resinas Bulk-fill, una resina compuesta convencional sobre la microdureza Vickers y la profundidad de curado de estas resinas. Se utilizaron tres composites Bulk-Fill-SDR Plus (SDR), Estelite BULK FILL Flow (EST), Admira® Fusion x-tra (AFX), y una resina compuesta convencional G-ænial POSTERIOR (GP) como grupo de control. Las muestras se obtuvieron a temperatura ambiente (24°C) y a 55°C en modo T2 después de haber sido colocadas en un dispositivo de calentamiento durante 10 minutos. Se dividieron en ocho grupos (n=10) según el tipo de material y el proceso de calentamiento que se utilizó (precalentado y no calentado). Se probaron con un medidor de microdureza Vickers (VHN) en las superficies inferior y superior. Las primeras mediciones se obtuvieron en la línea de base; la segunda se realizó después de que las muestras se almacenaran en agua destilada a 37°C durante 24 horas. La profundidad de curado se calculó utilizando una relación de dureza inferior/ superior de las mediciones. El análisis estadístico se realizó utilizando el SPSS V23 y las pruebas de Shapiro-Wilk. Por último, se utilizó la prueba de Duncan para las comparaciones múltiples (p<0,05). VHN aumentó tras el procedimiento de precalentamiento en las resina Bulk-Fill, disminuyó en los GP. No hubo diferencias entre los valores de VHN de referencia y de 24 horas en SDR y GP. Después de 24 horas, mientras que el VHN de EST aumentó, el VHN de AFX disminuyó. No hubo diferencias entre los ratios de dureza de las muestras de AFX y EST (p<0,001) y los ratios de dureza fueron mayores que los de GP y SDR. Al comparar los valores de referencia y los de 24 horas, el VHN dependió del tipo de materiales. Se obtuvo una profundidad de curado suficiente en todos los grupos con un grosor de 2mm.

Determinação do tempo de pré-aquecimento do leite humano ordenhado na pasteurização / Determinación del tiempo de precalentamiento de la leche humana extraída en la pasteurización / Determination of preheating time of expressed human milk in pasteurization

Esta Norma Técnica tem por objetivo estabelecer a determinação do tempo de pré-aquecimento do leite humano ordenhado no processo de pasteurização, visando a garantia da qualidade em Bancos de Leite Humano e sua certificação.

Esta Norma Técnica tiene como objetivo establecer la determinación del tiempo de precalentamiento de la leche humana extraída en el proceso de pasteurización, con el fin de asegurar la calidad en los Bancos de Leche Humana y su certificación.

In Vitro Effect of Temperature on Dentin Bond Strength of Universal Adhesive Systems / Efecto In Vitro de la temperatura sobre la resistencia de unión de los sistemas adhesivos universales a la dentina

ABSTRACT The aim of this study was to evaluate the shear bond strength (SBS) of two universal adhesives (Universal Single Bond and All Bond Universal) and a two- step self-etch adhesive system (Clearfil SE Bond) to dentine at various temperatures. Materials and Methods: One hundred and twenty dentin specimens were divided randomly to 12 groups, according to adhesive systems (Universal Single Bond and All Bond Universal, Clearfil SE Bond) and temperature ( 4ºC, 20 ºC, 36ºC, 55ºC) used. Dentin specimens were prepared (n :10, adhesives were applied, and composite cylinders were polymerized. Statistical analysis of the SBS data was performed using Two-way analysis of variance (ANOVA) and Tukey's Honestly Significant Differences post-hoc test. Results: The Clearfil SE Bond was shown to have higher SBS than the universal adhesives at all temperatures; however, there was no statistically significant difference (P>0.05). In both groups, the lowest SBS values were observed in the samples at 4°C while the highest SBS values were observed in the samples at 55°C. In this case, there was a statistically significant difference (P<0.05). Conclusions: The results suggest that the effectiveness of an adhesive may increase if it is preheated at 36°C or above before use instead of being used immediately after removal from the refrigerator or at room temperature.

RESUMEN El objetivo de este estudio fue evaluar la resistencia al cizallamiento (SBS) de dos adhesivos universales (Universal Single Bond y All Bond Universal) y un sistema de adhesivo de autograbado de dos pasos (Clearfil SE Bond) a la dentina en diferentes temperaturas. Materiales y métodos: Ciento veinte muestras de dentina se dividieron aleatoriamente en 12 grupos, de acuerdo con los sistemas adhesivos (Universal Single Bond y All Bond Universal, Clearfil SE Bond) y la temperatura (4ºC, 20ºC, 36ºC, 55ºC) utilizada. Se prepararon muestras de dentina (n: 10), se aplicaron los sistemas adhesivos y se polimerizaron los cilindros compuestos. El análisis estadístico de los datos de SBS se realizó utilizando el análisis de varianza de dos vías (ANOVA) y la prueba post-hoc de Tukey's. Resultados: El Clearfil SE Bond mostró tener un SBS más alto que los adhesivos universales en todas las temperaturas evaluadas; sin embargo, no hubo una diferencia estadísticamente significativa (P> 0.05). En todos los grupos, los valores más bajos de SBS se observaron en las muestras a 4°C, mientras que los valores de SBS más altos fueron obtenidos en las muestras a 55°C (P <0.05). Conclusiones: Los resultados sugieren que la efectividad de un adhesivo puede aumentar si se precalienta a 36°C o superior, antes de usarlo inmediatamente después de sacarlo del refrigerador o a temperatura ambiente.